PARAPURE™ Multi-purpose Acrylic Film

Acrylic Films Supporting Future Manufacturing

PARAPURE™ is an acrylic film that combines high Weatherability and transparency with excellent processability.

It can be used in a wide range of fields, including automotive parts.

Challenges with our unique resin development technology

Since we manufacture consistently from upstream, we can design formulations from monomers and resins.

Overcomes weaknesses of conventional films

The melt-extrusion technology cultivated in the sheet business is utilized to produce films with high smoothness and few defects.

Highest transparency
It is more transparent than glass and boasts the highest level of total light transmission as a film.
Good whitening resistance and workability
Transparency is not lost even after bending, and processing is easy.
Printing process available
Designs can be imparted by printing, vapor deposition, or other methods and used for various molded products.
Excellent Weatherability
It is resistant to deterioration even when used outdoors for long periods of time, and also prevents the deterioration of design parts due to ultraviolet rays.
Providing the best materials for each application
Not only do we offer a variety of thicknesses and widths, but we can also propose solutions to meet customer needs, such as multi-layer films with other materials.

HI Grade

High surface hardness (pencil hardness: H), clear type

LH Grade

Matte type with edge whitening suppressed during injection molding

Grade				HI Applications: Automotive Clear type			LH Applications: Automotive matte type
Thickness*				75	125	200	53
Test Item	Unit		test procedure
Total Light Transmittance	%		ISO 13468	92	92	92	-
Haze	%		ISO 13468	0.8	0.6	0.5	-
	Original fabric (roll)	%	JIS K 7136	-	-	-	31
	140℃ After heating	%	JIS K 7136	-	-	-	47
60° Gloss	Original fabric (roll)	%	JIS Z 8741	-	-	-	50
60° Gloss	140℃ After heating	%	JIS Z 8741	-	-	-	28
Glass Transition Temperature (Tg)	℃		JIS K 7121	112	112	112	-
Glass Transition Temperature (Tg)	MD	℃	JIS K 7121	-	-	-	103
Pencil Hardness	‐		ISO 15184	H	H	H	<6B
Young's Modulus	MD	Mpa	ISO 527-3	2300	2300	‐	-
Young's Modulus	MD/TD	-	JIS K 7127	-	-	-	1670
Tensile Yield Strength	MD/TD	Mpa	ISO 527-3	60/60	60/60	58/57	-
Tensile Yield Strength	MD/TD	Mpa	JIS K 7127	-	-	-	45/44
Tensile Breaking Strength	MD/TD	Mpa	ISO 527-3	50/50	60/60	58/57
Tensile Breaking Strength	MD/TD	Mpa	JIS K 7127	-	-	-	42/40
Tensile Elongation at Break	MD/TD	%	ISO 527-3	20/10	10/10	5/5	-
Tensile Elongation at Break	MD/TD	%	JIS K 7127	-	-	-	33/24
Dimensional Change (Heating Shrinkage)	MD/TD	%	ISO 11501	-1/0	-1/0	-	-0.4/0
MIT Foldability	MD/TD	Times	ISO 5626	70/50	20/10	-	1127/797

* Please inquire for other thicknesses and widths.

Note: The property values shown are typical values and are not guaranteed.

Please click here for information on FB grade of developed products.